Light-emitting device comprising a gallium-nitride-group compound-semiconductor

ABSTRACT

In the light-emitting gallium-nitride-group compound semiconductor devices using a substrate, the operating voltage is lowered and at the same time the occurrence of crack during crystal growth is suppressed, resulting in an improved manufacturing yield rate. The device includes a stacked structure of an n-type layer, a light-emitting layer and a p-type layer formed in the foregoing order on a substrate, and an n-side electrode formed on the surface of the n-type layer. The n-type layer is a laminate layer composed of, in the order from the substrate, first n-type layer and a second n-type layer having a carrier concentration higher than that of the first n-type layer. As the contact resistance between the n-type layer and the n-side electrode formed thereon is reduced, the operating voltage of a light-emitting device is lowered, and the power consumption decreased.

This is a continuation-in-part of U.S. application Ser. No. 09/219,428filed Dec. 23, 1998 and issued as U.S. Pat. No. 6,497,944 on Dec. 24,2002, and claims priority to Japanese Application No. JP9-359616 filedDec. 26, 1997.

BACKGROUND OF THE INVENTION

The present invention relates to a light-emitting device made withgallium-nitride-group compound-semiconductor such as light-emittingdiode, laser diode, etc.

Gallium-nitride-group compound-semiconductors have been increasinglyused as the semiconductor material for the visible light-emittingdevices and for use in the electronic devices of high operatingtemperature. The development has been significant in the field of blueand green light-emitting diodes.

In manufacturing the gallium-nitride-group compound-semiconductorsdevices, an insulating sapphire is generally used as the substrate forgrowing semiconductor film. Such devices are different from thelight-emitting devices where semiconductor substrates other thangallium-nitride-group type substrates, such as, for example GaAs orInGaP, are utilized. Specifically, those using an insulating substratelike the present sapphire have the n-side and p-side electrodes formedin one side of the substrate wherein the semiconductor film has beenformed, because the electrodes can not be provided from the substrate.

Meanwhile, in the recent manufacture of light-emitting devices,including those using the sapphire substrate, the growing ofgallium-nitride-group semiconductor thin film by a metal organic CVDmethod has become a main stream procedure. In the procedure, a substrateis placed in a reaction tube, and metal organic compound gas(trimethyl-gallium [TMG], tri-methyl-aluminum [TMA], tri-methyl-indium[TMI], etc.) are supplied therein as the material gas for the Group IIIelement, and ammonia, hydrazine, etc. as the material gas for the GroupV element, while maintaining the substrate at a high temperature 900°C.-1100° C., to have an n-type layer, a light-emitting layer and ap-type layer grown on the substrate in a stacked structure. After thelayers are grown and formed, the p-type layer and the light-emittinglayer are partially etched off to have the n-type layer exposed, andthen an n-side electrode and a p-side electrode are formed on thesurface of exposed n-type layer and the p-type layer, respectively, forexample by a deposition method.

Most of the recent light-emitting devices have the above describeddouble-hetero-structure, fabricated by stacking the thin films ofgallium-nitride-group compound-semiconductor on a sapphire substrate.FIG. 2 shows a cross sectional structure of a prior art light-emittingdevice of gallium-nitride-group compound-semiconductor.

In FIG. 2, a buffer layer 12, an n-type layer 13 of gallium-nitride(GaN), a light-emitting layer 14 of indium-gallium-nitride (InGaN), ap-type clad layer 15 of aluminum-gallium-nitride (AlGaN) and a p-typecontact layer 16 of GaN are stacked on a sapphire substrate 11. A p-sideelectrode 17 is formed on the p-type contact layer 16, and an n-sideelectrode 18 is formed on an exposed surface of the n-type layer 13provided by partially removing the following three layers, p-typecontact layer 16, p-type clad layer 15 and light-emitting layer 14. Then-type electrode 18 is normally made with aluminum (Al), titanium (Ti),gold (Au), or such other metals. The light-emittinggallium-nitride-group compound-semiconductor devices of the abovestructure have been disclosed in, for example, Japanese PatentPublication No. 6-268259.

In the prior art light-emitting gallium-nitride-groupcompound-semiconductor devices of the above structure, the n-type layer13 is formed of a gallium-nitride-group compound-semiconductor dopedwith n-type impurities such as silicon (Si), germanium (Ge). Morespecifically, during the growth of the n-type layer ofgallium-nitride-group compound-semiconductor by said metal organic CVDmethod, silane, mono-methyl-silane, etc. are supplied, together with thematerial gas, as material gas for Si, or germane, mono-methyl-germane,etc. as material gas for Ge. The carrier concentration of n-type layer13 may be controlled by adjusting the flow rate of the material gas forn-type impurities.

In the gallium-nitride-group compound-semiconductor, the n-type layermay also be formed by intentionally not doping the n-type impurities,because it exhibits the n-type property even without the n-typeimpurities being doped therein.

If in the light-emitting gallium-nitride-group compound-semiconductordevices the efficiency of light-emission is to be maintained high, theoperating voltage needs to be lowered. In order to reduce the operatingvoltage, the series resistance in respective layers ofcompound-semiconductor stacked on the substrate 11 and the contactresistance with electrode have to be made low.

An effective means for reducing the series resistance of n-type layer 13and the contact resistance with the n-side electrode 18 is to increasethe doping quantity of n-type impurities during growth of n-type layer13 by metal organic CVD. However, when doping quantity of the n-typeimpurities is increased, a strain can be generated in the grown n-typelayer 13, which increases and readily leads to cracks at the n-typelayer 13. If there are cracks in the n-type layer 13, an even emissionof light may not be obtained over the entire surface, and thereliability of a light-emitting device may be degraded.

On the other hand, if priority is placed on suppression of cracks atn-type layer 13, the n-type layer 13 needs to be grown and formed in areduced doping quantity of the n-type impurities. In this case, however,it becomes difficult to reduce the contact resistance with n-sideelectrode 18. If, in compensation of the above, the layer thickness ofthe n-type layer 13 is increased up-to about several μm (e.g. 16, 17 μm)in order to reduce the series resistance of a light-emitting device,cracks are easily induced like in the earlier described case. Inaddition, it needs a longer time for growing the crystal, which is anadditional disadvantage in the manufacture thereof.

As described in the above, if in a light-emitting gallium-nitride-groupcompound-semiconductor device the doping quantity of n-type impuritiesis increased for lowering the operating voltage, or the layer thicknessis increased, the occurrence of cracks may be unavoidable, which leadsto a degraded light-emitting capability and a deteriorated manufacturingyield rate.

The problems expected to be solved by the present invention with alight-emitting gallium-nitride-group compound-semiconductor device usingan insulating substrate are; first to reduce the operating voltage, andsecond to suppress the occurrence of cracks during growth for animproved manufacturing yield rate.

SUMMARY OF THE INVENTION

A novel invented light-emitting gallium-nitride-groupcompound-semiconductor device of the present invention has a stackedstructure comprising an n-type layer, a light-emitting layer and ap-type layer formed one after the other on an insulating substrate. Inaccordance with the present invention, the p-type layer andlight-emitting layer are partially removed from the surface of thestacked structure formed on the substrate such that the n-type layer isexposed, and then an electrode is formed on the exposed surface of then-type layer. The n-type layer contains, in order from the substrate, atleast a first n-type layer and a second n-type layer whose carrierconcentration is higher than that of the first n-type layer. Theelectrode is disposed on the second n-type layer.

With the above structure, a light-emitting gallium-nitride-groupcompound-semiconductor device is formed, in which the operating voltageis low and the manufacturing yield rate is high.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross sectional view shows the structure of a light-emittinggallium-nitride-group compound-semiconductor device in accordance withan exemplary embodiment of the present invention.

FIG. 2 is a cross sectional view shows one of the structures of a deviceof a light-emitting gallium-nitride-group compound-semiconductor in aprior art.

FIG. 3 is a sectional view showing a structure of semiconductor lightemitting device of gallium nitride compound in another embodiment of theinvention.

DETAILED DESCRIPTION OF THE INVENTION

A first exemplary embodiment of the light-emitting gallium-nitride-groupcompound semiconductor device of the present invention has a stackedstructure comprising an n-type layer, a light-emitting layer and ap-type layer formed one after the other on an insulating substrate. Thep-type layer and light emitting layer are partially removed from thesurface of the stacked structure formed on the substrate to expose then-type layer, and an electrode is formed on the exposed surface ofn-type layer. The n-type layer comprises, in the order from thesubstrate, at least a first n-type layer and a second n-type layer whosecarrier concentration is higher than that of the first n-type layer. Theelectrode is disposed on the second n-type layer. As a result of thepresent invention, the operating voltage of the light-emitting device islowered through a reduced contact resistance between the n-type layerand the n-side electrode.

In a second embodiment of the light-emitting device of the presentinvention the carrier concentration of the first n-type layer is setwithin a range 1×10¹⁶-2×10¹⁸ cm⁻³, and the carrier concentration of thesecond n-type layer within a range 2×10¹⁸-1×10¹⁹ cm⁻³. As a result, theoccurrence of cracks is suppressed and the contact resistance betweenthe n-type layer and the electrode is reduced.

In a third embodiment of the light-emitting device of the presentinvention the thickness of the second n-type layer is smaller than thatof the first n-type layer. As such, the occurrence of cracks issuppressed.

In a fourth embodiment of the light-emitting device of the presentinvention the layer thickness of the first n-type layer is set within arange of 1-5 μm, the thickness of the second n-type layer is set withina range of 0.1-0.5 μm. By specifying a range in the thickness of n-typelayer, the occurrence of cracks is effectively suppressed, and the depthof etching can be maintained with a high precision when removing a partof the p-type layer and the light-emitting layer for exposing thesurface of the n-type layer.

Next, the exemplary embodiments of the present invention are describedwith reference to the drawing.

FIG. 1 is a cross sectional view used to show the structure of alight-emitting gallium-nitride-group compound-semiconductor device inaccordance with an exemplary embodiment of the present invention.

In FIG. 1, a buffer layer 2 is formed on a substrate 1 made of sapphire.The buffer layer 2 may be formed of GaN, GaAlN, AlN, AlInN, etc. Stackedon the buffer layer 2 are, in the order from the bottom, an n-type layer3, a light-emitting layer 4, a p-type clad layer 5 and a p-type contactlayer 6. The n-type layer 3 has a laminate structure comprising, in theorder from the substrate 1, a first n-type layer 31 of lower carrierconcentration and a second n-type layer 32 of higher carrierconcentration. Si, Ge, etc. may be used as n-type impurities for formingthe n-type layer 3.

The light-emitting layer 4 of InGaN may be formed either by doping zinc,Si, etc. for making use of the impurity level; or leaving it as theun-doped, keeping thinner than 10 nm, for making use of the quantumlevel. “Un-doped” means the one in which neither p-type impurities norn-type impurities are added during the growth process.

The p-type clad layer 5 can be formed of AlGaN, GaN, AlGaInN, etc. Thep-type contact layer 6 may be formed of GaN, InGaN, etc. The p-typeimpurities to be doped in the p-type clad layer 5 and the p-type contactlayer 6 are Mg.

A p-side electrode 7 is provided on the p-type contact layer 6, and ann-side electrode 8 is provided on the second n-type layer 32 among then-type layers 3. The n-side electrode 8 may be formed of aluminum(Al),titanium(Ti), etc.

As described earlier, if in the manufacture of a light-emittinggallium-nitride-group compound-semiconductor device the doping quantityof n-type impurities in the n-type layer is increased or the thicknessof n-type layer is increased for the purpose of lowering the operatingvoltage, the frequency of the generation of cracks during growingprocess increases, and the manufacturing yield rate decreases. One ofthe reasons for the generation of cracks is believed to be attributableto a strain created in the n-type layer grown by doping n-typeimpurities with high concentration, and the amount of strain increasesalong with the increasing thickness of the layer.

Namely, in a prior art technology there was a tradeoff between theamount of doping of the n-type impurities and the thickness of n-typelayer regarding the occurrence of cracks. When attempting to lower theoperating voltage through optimization of the amount of n-typeimpurities to be doped in the n-type layer and the thickness of thelayer. Hence, there was a limitation in the conventional technology. Inother words, because there is a tradeoff in the relationship between thedoping amount of n-type impurities in the n-type layer and the layerthickness with respect to occurrence of cracks in n-type layer,attempting to lower the operating voltage through the optimization ofthe foregoing factors has a limitation.

In the present embodiment where the n-type layer 3 has a laminatestructure comprising, in the order from the substrate 1, a first n-typelayer 31 of lower carrier concentration and a second n-type layer 32 ofhigher carrier concentration, and the n-side electrode 8 is disposed onthe second n-type layer 32, the operating voltage can be lowered whilekeeping the manufacturing yield rate high. Detailed description is madein the following.

A light-emitting gallium-nitride-group compound-semiconductor device ofthe present exemplary embodiment is shown in FIG. 1. As stated, thedevice comprises an n-type layer 3 having a laminate structurecomprising, in the order from the substrate 1, a first n-type layer 31of lower carrier concentration and a second n-type layer 32 of highercarrier concentration. Namely, the first n-type layer 31 of lowercarrier concentration is formed on the substrate 1, and then the secondn-type layer 32 of higher carrier concentration is formed thereon. Then-side electrode 8 is formed on the second n-type layer 32.

In the above laminate structure where the first n-type layer 31 and thesecond n-type layer 32, the carrier concentration of respective layersbeing different, are formed one on the other in the order from thesubstrate 1, the first n-type layer 31 can be formed thick with thedoping quantity of n-type impurities in the first n-type layer 31decreased for a low carrier concentration. Therefore, both the increaseof resistance in the first n-type layer and the occurrence of cracks issuppressed. By disposing the n-side electrode 8 on the second n-typelayer 32 which has been formed on the first n-type layer 31 with then-type impurities doped more than in the first n-type layer 31 for ahigher carrier concentration, the contact resistance between the secondn-type layer 32 and the n-side electrode 8 is reduced. Therefore, theoperating voltage of a light-emitting device is lowered and the powerconsumption reduced.

As described in the above, each of the respective first and secondn-type layers 31, 32 have different carrier concentrations. This enablesthe optimization in both the lowering of operating voltage and theprevention of cracks. According to the results of experiments, preferredvalues of carrier concentration have been determined to be as follows.

It is preferred that the carrier concentration of the first n-type layer31 be within a range of 1×10¹⁶ cm⁻³-2×10¹⁸ cm⁻³. When the carrierconcentration of first n-type layer 31 is lower than 1×10¹⁶ cm⁻³ theseries resistance of the first n-type layer 31 itself goes high and theoperating voltage of the device tends to go high; on the other hand,when the carrier concentration of first n-type layer 31 is higher than2×10¹⁸ cm³ it tends to invite the cracks.

It is preferred that the carrier concentration of the second n-typelayer 32, whose carrier concentration is higher than that of the firstn-type layer 31, is in the range of 2×10¹⁸ cm⁻³-1×10¹⁹ cm⁻³. When thecarrier concentration of second n-type layer 32 is smaller than 2×10¹⁸cm⁻³ the contact resistance with the n-side electrode 8 can not bereduced low enough. On the other hand, when the carrier concentration ofsecond n-type layer 32 is greater than 1×10¹⁹ cm⁻³ the crystallinity ofthe layer tends to be degraded. This may deteriorate the crystallinityof light-emitting layer and a p-type layer to be grown thereon, and thelight-emitting output can be degraded.

Further, it is preferred that the thickness of second n-type layer 32has a thickness smaller than that of the first n-type layer 31.Specifically, the thickness of second n-type layer should preferably bewithin a range of 0.1-0.5 μm. If it is thinner than 0.1 μm, it becomesdifficult to control the etching depth in the process of partiallyremoving the p-type layer comprising the p-type clad layer 5 and p-typecontact layer 6 as well as the light-emitting layer 4 for having thesurface of n-type layer 3 exposed. If it is thicker than 0.5 μm, thecrystallinity of second n-type layer 32 is degraded, and thecrystallinity of a light-emitting layer 4, a p-type clad layer 5 and ap-type contact layer 6 to be grown on the second n-type layer 32 arealso degraded. Thus, the light-emitting output can be degraded.

The thickness of first n-type layer 31 should preferably be within arange 1-5 μm. If it is thinner than 1 μm, the series resistance of thedevice goes high to a raised operating voltage. If the first n-typelayer is thicker than 5 μm, the cracks may readily occur.

EMBODIMENT

An exemplary method for manufacturing an invented light-emittingsemiconductor device is described below.

The present exemplary embodiment refers to a method of growing agallium-nitride-group compound-semiconductor using a metal organic CVDprocess.

Embodiment 1

Description is made with reference to FIG. 1.

A sapphire substrate 1 having a mirror-polished surface is set on asubstrate holder within a reaction tube. The substrate 1 is maintainedat 1100° C. on the surface for 10 minutes, and is cleaned to removeorganic stains or humidity sticking on the surface by heating thesubstrate in a hydrogen gas flow.

Then, the surface temperature of substrate 1 is lowered down to 600° C.,and a buffer layer 2 of AlN is grown to the thickness of approximately25 nm by providing nitrogen gas, as the main carrier gas, at 10liter/min., ammonia at 5 liter/min., a TMA (tri-methyl-aluminum) carriergas containing tri-methyl-aluminum at 20 cc/min.

The supply of the TMA carrier gas is discontinued and the temperature israised up-to 1050° C. Then, while continuing the flow of nitrogen gas,as the main carrier gas, at 9 liter/min., and hydrogen gas at 0.95liter/min., new gases are added, namely, a carrier gas oftri-methyl-gallium (TMG) at 4 cc/min., a 10 ppm SiH4 (mono-silane) gas,as the source of Si, at 10 cc/min. for a duration of 60 min. in order togrow a first n-type layer 31 of Si doped GaN in the thickness ofapproximately 2 μm. As the result, the carrier concentration of firstn-type layer 31 is 1×10¹⁸ cm⁻³.

After the first n-type layer 31 is grown and formed, while keeping therespective flow rates of the main carrier gas and the TMG carrier gas asthey are, the flow rate of SiH4 gas alone is modified to 50 cc/min. tobe continued for 6 min. in order to grow a second n-type layer 32 of Sidoped GaN in the thickness of 0.2 μm. As the result, the carrierconcentration of the second n-type layer 32 is 5×10¹⁸ cm⁻³.

After the second n-type layer 32 is grown and formed, flow of the TMGcarrier gas and the SiH4 gas are discontinued, the surface temperatureof substrate 1 is lowered down to 750° C., and new gases are provided;nitrogen gas, as the main carrier gas, at 10 liter/min., a TMG carriergas at 2 cc/min., and a TMI (tri-methyl-indium) carrier gas at 200cc/min. for a duration of 30 sec. in order to grow a light-emittinglayer 4 of un-doped InGaN in the thickness of approximately 3 nm.

After the light-emitting layer 4 is formed, the TMI carrier gas and theTMG carrier gas are discontinued, the surface temperature of substrate 1is raised up-to 1050° C., and new gases are provided; nitrogen gas, asthe main carrier gas, at 9 liter/min., hydrogen gas at 0.94 liter/min.,a TMG carrier gas at 4 cc/min., a TMA carrier gas at 6 cc/min., acarrier gas for bis-cyclo-pentadienyel-magnesium (Cp₂Mg), or Mg source,at 50 cc/min. for a duration of 4 min. in order to grow a p-type cladlayer 5 of Mg doped AlGaN in the thickness of approximately 0.1 μm.

Then, the TMA carrier gas alone is discontinued, and at 1050° C., newgases are provided, namely, nitrogen gas, as the main carrier gas, at 9liter/min., hydrogen gas at 0.90 liter/min., a TMG carrier gas at 4cc/min., a Cp₂Mg carrier gas at 10 cc/min., for a duration of 3 min. inorder to grow a p-type contact layer 6 of Mg doped GaN in the thicknessof approximately 0.1 μm. After the p-type contact layer 6 is grown, theTMG carrier gas, as a material gas, and ammonia are discontinued. Thewafer is then cooled down to room temperature while the flow of nitrogengas and the hydrogen gas are maintained as is, and then the wafer istaken out from the reaction tube.

On the surface of the stacked layer structure containing a quantum wellstructure thus formed of gallium-nitride-group compound semiconductor,an SiO₂ film is deposited by CVD process. Then, an etching mask ispatterned in a certain specific shape by photolithography. The p-typecontact layer 6, the p-type clad layer 5 and the light-emitting layer 4are etched off in part by a reactive ion etching process for a depth ofapproximately 0.25 μm to have the surface of second n-type layer 32exposed. On the exposed surface of second n-type layer 32 an n-sideelectrode 8 of Al is deposited and formed through photolithography anddeposition processes. By the same procedure, a p-side electrode 7 of Niand Au is deposited and formed on the surface of the p-type contactlayer 6.

The reverse surface of the sapphire substrate 1 is polished down toapproximately 100 μm thick, and separated into chips by scribing. Eachof the chips is attached on a stem with the surface having the electrodeformed thereon. The respective n-side electrode 8 and p-side electrode 7on the chip are connected with wire to electrodes of the stem, and thewhole structure is resin-molded to complete a light-emitting diode. Whenthe light emitting diode is driven with 20 mA forward current, it emitsa blue-violet light of 430 nm wave-length; the forward operating voltageat that time was 3.4V.

As a comparative specimen 1, a light-emitting diode has beenmanufactured in the same procedure as in embodiment 1, except that; inthe process for growing a first n-type layer 31 and a second n-typelayer 32 of embodiment 1, an n-type layer 3 of Si doped GaN having asingle layered structure has been grown by providing, at 1050° C.,nitrogen gas, or the main carrier gas, at 9 liter/min., hydrogen gas at0.95 liter/min., a TMG carrier gas at 4 cc/min., SiH4 gas at 10 cc/min.,for a duration of 66 min.

In a light-emitting diode manufactured through the procedure ofcomparative specimen 1, the carrier concentration of the n type layerwas 1×10¹⁸ cm⁻³. When it is driven with 20 mA forward current, itemitted, like that of embodiment 1, blue-violet light of 430 nmwave-length. However, the forward operating voltage at that time was4.0V, or 0.6V higher than in embodiment 1.

Embodiment 2

A light emitting diode has been manufactured in the same procedure as inembodiment 1, except that; in the process for growing a first n-typelayer 31 of embodiment 1, a first n-type layer 31 of Si doped GaN hasbeen grown in the thickness of approximately 1 μm, by providing, at1050° C., nitrogen gas, as the main carrier gas, at 9 liter/min.,hydrogen gas at 0.95 liter/min., a TMG carrier gas at 4 cc/min., SiH4gas at 20 cc/min., for a duration of 30 min. After the first n-typelayer 31 is grown and formed, the flow rate of the SiH4 gas alone wasmodified to 100 cc/min. to be provided by a duration of 3 min., whilethe respective flow rate of the main carrier gas and the TMG carrier gashave been maintained as they are, in order to grow a second n-type layer32 of Si doped GaN in the thickness of approximately 0.1 μm.

The carrier concentration in the present exemplary embodiment 2 of therespective first n-type layer 31 and the second n-type layer 32 were2×10¹⁸ cm⁻³ and 1×10¹⁹ cm⁻³. When it is driven with 20 mA forwardcurrent, it emits blue-violet light of 430 nm wavelength; and theforward operating voltage at that time was 3.3V.

As a comparative specimen 2, a light-emitting diode has beenmanufactured in the same procedure as in embodiment 2, except that; inthe process for growing a first n-type layer 31 and a second n-typelayer 32 of embodiment 2, an n-type layer of Si doped GaN having asingle layered structure has been grown by providing, at 1050° C.,nitrogen gas, as the main carrier gas, at 9 liter/min., hydrogen gas at0.95 liter/min., a TMG carrier gas at 4 cc/min., SiH₄ gas at 100cc/min., for a duration of 33 min.

In a light-emitting diode manufactured through the procedure ofcomparative specimen 2, the carrier concentration of the n-type layerwas 1×10¹⁹ cm⁻³. When it is driven with 20 mA forward current, it emits,unlike that of embodiment 2, blue-white light. In a microscopicobservation conducted to study the state of emitting the light, it hasbeen confirmed that the light was emitted only at a part of thecircumferential portion of the n-type electrode. This seems to have beencaused by cracks in the n-type layer. The forward operating voltage ofthe light-emitting diode of comparative specimen 2, when driven with 20mA forward current, was 4.8V, or 1.5V higher than in embodiment 2.

Embodiment 3

A light-emitting diode has been manufactured in the same procedure as inembodiment 1, except that; in the process for growing a first n typelayer 31 of embodiment 1, a first n-type layer 31 of Si doped GaN hasbeen grown in the thickness of approximately 5 μm, by providing, at1050° C., nitrogen gas, as the main carrier gas, at 9 liter/min.,hydrogen gas at 0.95 liter/min., a TMG carrier gas at 4 cc/min., SiH₄gas at 1 cc/min., for a duration of 150 min. After the first n-typelayer 31 is grown and formed, the flow rate of the SiH₄ gas alone wasmodified to 20 cc/min. to be provided by a duration of 15 min., whilethe flow rate of the respective main carrier gas and the TMG carrier gashave been maintained as they are, in order to grow a second n-type layer32 of Si doped GaN in the thickness of approximately 0.5 μm.

The carrier concentration in the present exemplary embodiment 3 of therespective first n-type layer 31 and the second n-type layer 32 were1×10¹⁶ cm⁻³ and 2×10¹⁸ cm⁻³. When it is driven with 20 mA forwardcurrent, it emits blue-violet light of 430 nm wavelength; and theforward operating voltage at that time was 3.6V.

As a comparative specimen 3, a light-emitting diode has beenmanufactured in the same procedure as in embodiment 3, except that; inthe process for growing a first n-type layer 31 and a second n-typelayer 32 of embodiment 3, an n-type layer 3 of Si doped GaN having asingle layered structure has been grown by providing, at 1050° C.,nitrogen gas, as the main carrier gas, at 9 liter/min., hydrogen gas at0.95 liter/min., a TMG carrier gas at 4 cc/min., SiH₄ gas at 1 cc/min.,for a duration of 165 min.

In a light-emitting diode manufactured through the procedure ofcomparative specimen 3, the carrier concentration of the n-type layerwas 1×10¹⁷ cm⁻³. When it is driven with 20 mA forward current, itemitted, like in embodiment 3, blue-violet light of 430 nm wave-length.The forward operating voltage at that time was 4.7V, or 1.1V higher thanin embodiment 3.

Embodiment 4

A light-emitting diode has been manufactured in the same procedure as inembodiment 1, except that; in the process for growing a first n-typelayer 31 of embodiment 1, a first n-type layer 31 of un-doped GaN hasbeen grown in the thickness of approximately 4 μm, by providing, at1050° C., nitrogen gas, as the main carrier gas, at 9 liter/min.,hydrogen gas at 1 liter/min., a TMG carrier gas at 4 cc/min., for aduration of 120 min. After the first n-type layer 31 was grown, a secondn-type layer 32 of Si doped GaN has been grown in the thickness ofapproximately 0.3 μm, by providing, in succession, the main carrier gasat 9 liter/min., hydrogen gas at 0.90 liter/min., a TMG carrier gas at 4cc/min., and with an addition of SiH₄ gas at 100 cc/min., all of whichgases are supplied for a duration of 9 min.

The carrier concentration in the present exemplary embodiment 4 of therespective first n-type layer 31 and the second n-type layer 32 were2×10¹⁶ cm⁻³ and 1×10¹⁹ cm⁻³. When it is driven with 20 mA forwardcurrent, it emits blue-violet light of 430 nm wavelength; and theforward operating voltage at that time was 3.6V.

Embodiment 5

FIG. 3 is a sectional view showing a structure of semiconductor lightemitting device of gallium nitride compound in another embodiment of theinvention.

In FIG. 3, reference numeral 100 is a substrate, which is made of aconductive material. Preferred examples of the substrate 100 include GaNsubstrate mainly composed of GaN (containing additives such as Al, In,As, P), SiC substrate mainly composed of SiC, Si substrate mainlycomposed of Si, and AlN substrate mainly composed of AlN. Further, asshown in FIG. 1, sapphire or other insulating substrate may also be usedas the substrate 100.

In particular, when a GaN substrate mainly composed of GaN is used asthe substrate 100, it is preferred to form an n-layer 103 on thesubstrate directly because the n-layer 103 is also made of GaN or amaterial mainly composed of GaN. However, if the GaN substrate mainlycomposed of GaN is used as the substrate 100, either buffer layer 101 orinsertion layer 102 may be provided at the same time.

When an SiC substrate mainly composed of SiC or Si substrate mainlycomposed of Si is used as the substrate 100, it is preferred to form abuffer layer 101 in order to enhance the crystallinity of the layer tobe laminated in the upper part. In this case, too, an insertion layer102 may be disposed on the buffer layer 101 so as to enhance thecrystallinity further.

When an AlN substrate mainly composed of AlN is used as the substrate100, it is preferred to form an n-layer layer 103 directly on thesubstrate. The reason is that the n-layer 103 is made of GaN or amaterial mainly composed of GaN, and its lattice constant is close tothat of the substrate of AlN or material mainly composed of AlN, so thata favorable crystallinity is assured without provision of buffer layer101.

The buffer layer 101 may be composed of one layer of GaN, GaAlN, AlN,AlInN, or the like, or by laminated plural layers thereof. As mentionedabove, this buffer layer 101 is preferred to be provided when thelattice constant of the material used as the substrate 100 is differentfrom that of the layer laminated on the upper part.

The insertion layer 102 may be composed of one layer of undoped orn-type impurity doped GaN, AlGaN, InGaN, or AlGaInN, or by laminatingplural layers thereof, and by the provision of the insertion layer 102,the crystallinity of the layer formed in the upper part is improved, ordistortion is absorbed (crack is prevented) when forming a film, so thata favorable light emitting characteristic may be obtained.

As mentioned above, depending on the material of the substrate 100, bothbuffer layer 101 and insertion layer 102 may not be necessary, or onlyone of either the buffer layer 101 or the insertion layer 102 may beused. When using both buffer layer 101 and insertion layer 102, it ispreferred to laminate the buffer layer 101 and insertion layer 102 inthis sequence from the substrate 100 side.

Reference numeral 200 represents n-type layer laminated directly on thesubstrate 100 or on the substrate 100 by way of at least either bufferlayer 101 or insertion layer 102, and the n-type layer 200 has alaminated structure forming a first n-type layer 103 of low carrierconcentration, an insertion layer 104, and a second n-type layer 105 ofhigher carrier concentration than the first n-type layer 103sequentially from the substrate 100 side. As an n-type impurity forforming the n-type layer 200, Si or Ge may be used. Generally, since aGaN material is n-type conductive in an undoped state, the n-type layer103 may be also undoped.

The insertion layer 104 is one layer selected from undoped or n-typeimpurity doped GaN, AlGaN, InGaN, and AlGaInN, or is formed bylaminating plural layers thereof, and the insertion layer 104 improvesthe crystallinity of the layer formed in the upper part or absorbsdistortion (prevents crack) when forming the film, so that a favorablelight emitting characteristic may be obtained. The insertion layer 104may be omitted if the first n-type layer 103 is excellent incrystallinity or distortion is small between the first n-type layer 103and second n-type layer 105, and in such a case, the first n-type layer103 and second n-type layer 105 are bonded directly.

The carrier concentration of the insertion layer 104 is not closelyrelated with the carrier concentration of the first n-type layer 103 orcarrier concentration of the second n-type layer 105. That is, asmentioned above, the insertion layer 104 is intended to improve thecrystallinity of the second n-type layer 105 or absorb distortionbetween the first n-type layer 103 and second n-type layer 105.Preferably, the carrier concentration of the insertion layer 104 may beset higher than the carrier concentration of the first n-type layer 103,so that the current flowing in the n-type layer 200 also flows smoothlyin the first n-type layer 103, and the electric resistance of the n-typelayer 200 may be lowered and the efficiency may be enhanced. Further,preferably, the carrier concentration of the insertion layer 104 shouldbe lower than the carrier concentration of the second n-type layer 105.

Reference numeral 107 is a luminous layer, which is formed directly onthe second n-type layer 105 or laminated by way of an insertion layer106.

The luminous layer 107 composed of InGaN or other material may be dopedwith zinc or Si or the like, and a luminous layer making use of impuritylevel may also be formed, or it may be also formed as an undopedluminous layer of film thickness of 10 nm or less by making use ofquantum level. Specifically, it may be formed as a single quantum wellstructure composed of one layer of InGaN, or as a multiple quantum wellstructure composed by laminating at least two layers of InGaN layer andGaN layer alternately, or laminating at least two layers of InGaN layerdifferent in concentration of In alternately. Herein, an undopedcomposition refers to a film formed without adding p-type impurity orn-type impurity. If the luminous layer 107 is the multiple quantum wellstructure, the undoped luminous layer means the well layer is undoped,and it does not matter whether the barrier layer is doped or not.

The insertion layer 106 is formed by using at least one layer selectedfrom undoped or n-type impurity doped GaN, AlGaN, InGaN, and AlGaInN. Byusing one material only selected from the group, one layer or plurallayers may be laminated, or by laminating plural materials selected fromthe group, at least one layer may be composed of a different materialfrom the other layer.

By disposing the insertion layer 106, the crystallinity of the layerformed in the upper part may be improved, the diffusion concentration ofn-type impurity into the luminous layer 107 may be kept within anallowable range, or distortion can be absorbed (crack can be formed)when forming a film, so that a favorable light emitting characteristicmay be obtained. The insertion layer 106 may be omitted if the secondn-type layer 105 is excellent in crystallinity, the degree of diffusionof n-type impurity into the luminous layer 107 is small, or distortionis small between the luminous layer 107 and second n-type layer 105, andin such a case, the second n-type layer 105 and luminous layer 107 arebonded directly.

Reference numeral 109 is a p-type clad layer, which is directly bondedon the luminous layer 107, or disposed by way of an insertion layer 108.

As the p-type clad layer 109, one layer selected from AlGaN, GaN, andAlGaInN may be used, or plural layers selected from the group may belaminated. As a p-type contact layer 110 laminated on the p-type cladlayer 109, GaN, InGaN, or AlGaN may be used. As the p-type impurity tobe doped in the p-type clad layer 109 and p-type contact layer 110, Mgor the like may be used.

The insertion layer 108 is formed by using at least one layer selectedfrom undoped or p-type impurity doped GaN, AlGaN, InGaN, and AlGaInN.That is, by using one material only selected from the group, one layeror plural layers may be laminated, or by laminating plural materialsselected from the group, at least one layer may be composed of adifferent material from the other layer.

The insertion layer 108 is intended to prevent diffusion of p-typeimpurity into the luminous layer 107 or to enhance the hole mobility inthe insertion layer 108. This insertion layer 108 may be omitted ifprevention of diffusion of p-type impurity into the luminous layer 107can be realized by other means, the diffusion concentration of p-typeimpurity into the luminous layer 107 is in an allowable range, or thehole mobility in the p-type clad layer 109 is high.

On the p-type contact layer 110, a p-side electrode 111 is formed, whilean n-side electrode 112 is disposed on the second n-type layer 105 ofthe n-type layer 200. The material for forming the n-side electrode 112is aluminum (Al), titanium (Ti), or other metal. In this embodiment, thep-type layer is composed of a two-layer structure of p-type clad layer109 and p-type contact layer 110, but it may also be composed in asingle-layer structure or a multi-layer structure of three layers ormore.

Herein, in manufacture of semiconductor light emitting device of galliumnitride compound, it has been already explained that the frequency ofoccurrence of cracks when growing the film becomes high, therebylowering the manufacturing yield if the dopant of the n-type impurity inthe n-type layer is increased or the thickness of the n-type layer isincreased to reduce the operating voltage of the device. Such occurrenceof cracks seem to be caused by distortion formed in the n-type layergrown by doping the n-type impurity at high concentration and increaseof distortion amount by increasing the layer thickness.

It was a conventional technology that the decrease of operating voltageby optimizing the n-type impurity dopant amount and the layer thicknessof the n-type layer is limited because of existence of trade-off aboutoccurrence of cracks between the n-type impurity dopant amount and thelayer thickness of the n-type layer. In other words, since trade-offabout occurrence of crack in n-type layer exists between the n-typeimpurity dopant amount and the layer thickness of the n-type layer,decrease of operating voltage is limited if they are optimized.

By contrast, in this embodiment, the n-type layer 200 has a laminatedstructure including the first n-type layer 103 of low carrierconcentration and second n-type layer 105 of higher carrierconcentration sequentially from the substrate 100 side, and by themulti-layer structure of the n-type layer 200 disposing the n-sideelectrode 112 on the second n-type layer 105, the operating voltage canbe lowered and the manufacturing yield can be maintained at high level.This is explained below.

In the semiconductor light emitting device of gallium nitride compoundof the embodiment shown in FIG. 3, the n-type layer 200 has a laminatedstructure including the first n-type layer 103 of low carrierconcentration and second n-type layer 105 of higher carrierconcentration sequentially from the substrate 100 side. That is, afterforming the first n-type layer 103 of low carrier concentration at thesubstrate 100 side, the second n-type layer 105 of higher carrierconcentration is formed on the first n-type layer 103 either directly orby way of the insertion layer 104, and the n-side electrode 112 isformed on the second n-type layer 105.

By such laminated structure forming the first n-type layer 103 andsecond n-type layer 105 different in the carrier concentrationsequentially from the substrate 100 side, if the carrier concentrationis lowered by decreasing the n-type impurity dopant amount of the firstn-type layer 103, and first n-type layer 103 can be formed as a thickfilm, and increase of resistance and occurrence of crack in the firstn-type layer 103 can be suppressed at the same time. On the first n-typelayer 103, by forming the n-side electrode 112 on the second n-typelayer 105 heightened in the carrier concentration by increasing then-type impurity dopant amount larger than the first n-type layer 103,the contact resistance between the second n-type layer 105 and n-sideelectrode 112 can be decreased, and thereby the operating voltage of thelight emitting device can be lowered and the power consumption can besaved.

Thus, difference in the carrier concentration between the first andsecond n-type layers 103, 105 can encourage optimization in both aspectsof decrease of operating voltage and prevention of occurrence of cracks.Specific numerical definitions of the carrier concentrations are asfollows according to the knowledge of the present inventors.

The carrier concentration of the first n-type layer 103 is preferred tobe in a range of 1×10¹⁶ cm⁻³ to 2×10¹⁸ cm⁻³. As far as this carrierconcentration range is satisfied, the n-type layer 103 may be undoped.When the carrier concentration of this first n-type layer 103 is smallerthan 1×10¹⁶ cm⁻³, the series resistance by the first n-type layer 103itself increases, and the operating voltage of the device tends to behigher, or when the carrier concentration is larger than 2×10¹⁸ cm⁻³,cracks are likely to occur.

The carrier concentration of the second n-type layer 105 higher than thecarrier concentration of the first n-type layer 103 is preferred to be2×10¹⁸ cm⁻³ to 1×10¹⁹ cm⁻³. When the carrier concentration of thissecond n-type layer 105 is smaller than 2×10¹⁸ cm⁻³, it is hard todecrease the contact resistance to the n-side electrode 8 sufficiently,or when larger than 1×10¹⁹ cm⁻³, the crystallinity of the layer tends tobe worse, and the crystallinity of the luminous layer or p-type layergrown thereon becomes poor, and the light emitting output may decline.

The film thickness of the second n-type layer 105 should be smaller thanthat of the first n-type layer 103, preferably in a range of 0.1 to 0.5μm. If thinner than 0.1 μm, it is hard to control the depth of etchingfor exposing the surface of the n-type layer 3 by removing part of thep-type layer and luminous layer 107 by the p-type clad layer 109 andp-type contact layer 110. If thicker than 0.5 μm, the crystallinity ofthe second n-type layer 105 is poor, and the crystallinity of theluminous layer 107, p-type clad layer 109 and p-type contact layer 110grown on this second n-type layer 105 is impaired, and the lightemitting output may be lowered.

The film thickness of the first n-type layer 103 is preferred to be in arange of 1 to 5 μm. If thinner than 1 μm, the series resistance of thedevice increases and the operating voltage tends to be higher, or ifthicker than 5 μm, cracks are likely to occur.

One advantage of the present invention is that the contact resistancebetween the n-type layer and the n-side electrode formed thereon islowered by providing an n-type layer stacked on a substrate in atwo-layered structure composed of a first n-type layer of smallercarrier concentration and a second n-type layer of greater carrierconcentration. As a result, the operating voltage of a light-emittingdevice is lowered and the power consumption reduced.

Another advantage is that the occurrence of cracks in a light-emittingdevice is suppressed through a specified carrier concentration of therespective first and second n-type layers, in addition to reduction inthe power consumption.

In a variation of the foregoing, the occurrence of cracks in alight-emitting device can be suppressed through a specified relationshipin the layer thickness between the first and the second n-type layers.

In yet another variation, the occurrence of cracks can be effectivelysuppressed through a specified range of respective layer thicknessvalues in the first and the second n-type layers. In addition, the depthof etching, when partially etching the p-type layer and thelight-emitting layer off for having the surface of n-type layer exposed,can be maintained at a level of high precision.

Of course, it should be understood that a wide range of modificationscan be made to the exemplary embodiments described above. It istherefore intended that the foregoing detailed description be regardedas illustrative rather than limiting and that it be understood that itis the following claims, including all equivalents, which are intendedto define the scope of this invention.

1. A semiconductor light emitting device of gallium nitride compoundcomprising: a substrate, an n-type component composed of GaN or amaterial mainly made of GaN, disposed on said substrate directly or byway of other layer, an undoped luminous part disposed directly or by wayof other layer at the opposite side of the substrate side in said n-typecomponent, a p-type component disposed directly or by way of other layerat the opposite side of the n-type component side in said luminous part,and electrodes disposed in said p-type component and n-type componentindividually, wherein said n-type component has a first region and asecond region in a thickness direction, said first region and secondregion are disposed sequentially from the substrate side, the secondregion and substrate do not contact with each other, the first regionand second region are disposed directly or by way of other layer, thesecond region is set at a higher carrier concentration than the firstregion, and its carrier concentration is 2×10¹⁸ cm⁻³ to 1×10¹⁹ cm⁻³. 2.The semiconductor light emitting device of gallium nitride compound ofclaim 1, wherein an insertion layer composed of one layer of undoped orn-type impurity doped GaN, AlGaN, InGaN, or AlGalnN, or by laminatingplural layer thereof is disposed between the first region and secondregion of the n-type component.